Carbon And Glass Fiber Pultruded Profiles

Description

Carbon fiber and glass fiber/epoxy resin pultruded profiles are manufactured through a pultrusion process. A continuously processed composite material with high fiber content, high performance and low cost.
In the manufacturing process, the carbon fiber bundle is formed through a special impregnation and curing process.
Compared with other composite materials processing, the high fiber straightness achieved by pultrusion can provide excellent mechanical properties in the laminated structure.

Features: - Peel Ply Cover; - High Rigidity; - Low Porosity; - Wind Turbine Blade; - High Fiber Straightness

Add Inquiry (0)

PRODUCT SPECIFICATIONS

Resin	Fiber	Specification		Fiber Volume Content (%)
		Width (mm)	Thickness (mm)
Epoxy Resin	Carbon Fiber	50-200	1-8	58-72
	Glass Fiber
Vinyl Ester Resin	Carbon Fiber
	Glass Fiber

MECHANICAL PROPERTIES

Properties	Unit	Product Types			Test Standard
Properties	Unit	Carbon Fiber / Epoxy		Glass Fiber / Epoxy	Test Standard
Fiber Volume Content	%	60%	65%	70%	-
0°Tensile Strength	MPa	1700	2000	1500	ISO 527-5
0°Tensile Modulus	GPa	135	150	65	ISO 527-5
0° Compressive Strength	MPa	1050	1400	1500	ISO 14126
0°Compressive Modulus	GPa	130	145	60	ISO 14126
0°Flexural Strength	MPa	1200	1350	1300	ISO 14125
0°Flexural Modulus	GPa	140	145	60	ISO 14125

Note: The above information is for general reference only and cannot be used as a guarantee.